納米TiO2、ZrO2對苯基硅橡膠性能的影響研究

時間:2019-06-02 19:34來源:畢業論文
LED封裝用苯基硅橡膠材料的改性研究,通過在苯基硅橡膠中摻雜硅烷偶聯劑改性納米粒子 TiO2和ZrO2,系統研究了兩種納米粒子及其添加量對苯基硅橡膠的光學性能、電學性能、導熱性能

摘要 本文主要內容為 LED 封裝用苯基硅橡膠材料的改性研究,通過在苯基硅橡膠中摻雜硅烷偶聯劑改性納米粒子 TiO2和ZrO2,系統研究了兩種納米粒子及其添加量對苯基硅橡膠的光學性能、電學性能、導熱性能等的影響。研究表明:硅橡膠納米復合材料的折射率隨著粒子添加量增加而增加,當納米TiO2、ZrO2含量為 3wt%時,所制得的納米復合材料具有較好的折射率,分別為 1.573 和 1.571。改性納米粒子硅橡膠復合材料的介電常數較未改性納米粒子硅橡膠復合材料的高。 硅橡膠納米復合材料的體積電阻率隨著粒子的添加量增加而有所增加,當納米 ZrO2、TiO2的含量為3wt%時,所制得的納米復合材料具有最高的體積電阻率,添加改性 ZrO2、TiO2 的苯基硅橡膠復合材料的體積電阻率分別從2.6× 1013Ω•cm 左右分別增加到 17.97× 1013和26× 1013Ω•cm。橡膠納米復合材料的導熱率呈現先增加后減小的趨勢,當納米 ZrO2含量為 0.01wt%時而納米 TiO2的含為 0.6  wt%時,所制得的納米復合材料具有最佳的導熱率,分別為 0.199和0.215W• m-1• K-1。  35973
畢業論文關鍵詞:LED封裝;納米粒子;苯基硅橡膠;納米復合材料    
Research on Different Contents of PhenylSilicone Rubber Modified with Nanoparticles (TiO2\ZrO2) 
Abstract This article is mainly for a modification of Silicone Rubber nanocomposite materialused as encapsulant for LED packaging, by means of adding Nano-TiO2, ZrO2  surface-modified with silane coupling agent. Then, the mechanical properties, optical properties, dielectric properties, thermal conductivity of silicone rubber nanocomposites were systematically studied.  The research  results showed that  refractive index of the silicone rubber nanocomposites increased with particles content. When the nano TiO2  and ZrO2  content were 3wt%, the prepared nanocomposite kept good refractive index, which was 1.573 and 1.571 respectively.Thedielectric constant ofsilicone rubber nanocomposite withsurface-modified particles particles  increases with particles content  more than the nanocomposite without surface-modified particles.  When nano-ZrO2  and  TiO2  content  were  3wt%, the prepared nanocomposite  kept  the highest volume resistivity.The  volume resistivity  of  silicone rubber composites adding  with  modified ZrO2  and  TiO2increased  from 2.6×1013Ω•cm to 17.97×1013,26×1013Ω•cm respectively.Thermal conductivity of the phenyl silicone rubber nanocomposites increased firstly  and then decreases. when the nano-ZrO2  content  were 0.01wt%,and nano-TiO2  content were  0.6 wt%,  the  prepared nanocomposite  presented  best thermal conductivity, which were 0.199,and 0.215 W•m-1•K-1 respectively.  
源¥自%六:維;論-文'網=www.aftnzs.live

Keywords: LED packaging;Nanoparticles; Phenyl silicone rubber; Nanocomposite   
目錄
1緒論1
1.1LED簡介.1
1.1.1LED封裝介紹1
1.1.2LED封裝材料的研究意義3
1.1.3LED封裝材料的性能要求3
1.2LED封裝用材料的研究進展.4
1.2.1環氧樹脂.4
1.2.2有機硅改性環氧樹脂.4
1.2.3有機硅材料.5
1.3納米粒子有硅復合材料的研究進展.6
1.3.1TiO2、ZrO2納米粒子的性質.6
1.3.2無機納米粒子的表面修飾.6
1.3.3無機納米粒子在硅橡膠中的應用.8
1.3.4有機硅橡膠/無機納米復合材料的制備方法8
1.4課題研究的目的和意義.9
1.4.1研究目的.9
1.4.2研究意義.9
2實驗部分10
2.1實驗用主要原料.10
2.2實驗用儀器設備.10
2.3實驗過程11
2.3.1納米粒子TiO2和ZrO2的表面修飾11 納米TiO2、ZrO2對苯基硅橡膠性能的影響研究:http://www.aftnzs.live/huaxue/20190602/34211.html